Notes

Lignin-Based Gel Polymer Electrolyte for Cationic Conductivity.
Plasmon-enhanced photocatalysis has the potential to reduce activation energies and decrease temperature requirements, which increases catalyst stability and lowers process operating costs. The near-field enhancement that occurs at junctions between plasmonic nanoparticle clusters (i.e., hot spots) has been well-studied for sensing applications (e.g., Raman scattering). However, experimental insight into the effect of nanoparticle cluster hot spots on plasmon-enhanced photocatalysis is lacking. We demonstrate that catalytic activity is increased when clusters of gold nanoparticles (AuNPs) are formed relative to isolated particles using the same catalyst loading. Through experimental controls, we conclude that this catalytic enhancement is most likely due to the formation of plasmonic hot spots. Clusters of AuNPs were formed by adding L-cysteine to an AuNP dispersion, and a 20 ± 12% enhancement in the photocatalytic dye degradation rate was observed using a Fenton process. While this report may be a modest enhancement relative to the spectacular near-field electromagnetic field enhancements predicted by simulation at the nanoparticle junction, this finding supports the recent work of Srimanta et al. that plasmonic hot spots contribute to catalytic rate enchantments. It is anticipated that further self-assembly strategies to optimize interparticle orientations and cluster size distributions will improve the enhancement due to the formation of hot spots, and careful control will be required. For example, excess L-cysteine addition revealed extensive aggregation and subsequent rate reductions.Understanding how deprotonation impacts the photophysics of UV filters is critical to better characterize how they behave in key alkaline environments including surface waters and coral reefs. Using anion photodissociation spectroscopy, we have measured the intrinsic absorption electronic spectroscopy (400-214 nm) and numerous accompanying ionic photofragmentation pathways of the benzophenone-4 anion ([BP4-H]-). Relative ion yield plots reveal the locations of the bright S1 and S3 excited states. For the first time for an ionic UV filter, ab initio potential energy surfaces are presented to provide new insight into how the photofragment identity maps the relaxation pathways. These calculations reveal that [BP4-H]- undergoes excited-state decay consistent with a statistical fragmentation process where the anion breaks down on the ground state after nonradiative relaxation. The broader relevance of the results in providing a basis for interpreting the relaxation dynamics of a wide range of gas-phase ionic systems is discussed.Lateral single-layer transition metal dichalcogenide (TMD) heterostructures are promising building blocks for future ultrathin devices. Recent advances in the growth of coherent heterostructures have improved the structural precision of lateral heterojunctions, but an understanding of the electronic effects of the chemical transition at the interface and associated strain is lacking. Here we present a scanning tunneling microscopy study of single-layer coherent TMD heterostructures with nearly uniform strain on each side of the heterojunction interface. We have characterized the local topography and electronic structure of single-layer WS2/WSe2 heterojunctions exhibiting ultrasharp coherent interfaces. Uniform built-in strain on each side of the interface arising from lattice mismatch results in a reduction of the bandgap of WS2. Selleckchem U0126 By mapping the tunneling differential conductance across the interface, we find type-II band alignment and an ultranarrow electronic transition region only ∼3 nm in width that arises from wave function mixing between the two materials.Hydroxide ion conductivity is a key aspect of anion exchange membranes and is mainly determined by the nanoscale membrane morphologies. Fundamental understanding of the structural and transport properties of membranes in terms of polymer architectures is crucial for future development of membrane-based applications. Using mesoscale simulations, this work predicts the mesostructure of the hydrated triblock copolymers; the designed polymers are composed of aromatic (polyphenylene oxide, PPO) or aliphatic (polystyrene-ethylene-butylene-styrene, SEBS) backbones, with cationic side chains being modified by hydrophobic or hydrophilic spacers. For PPO-based polymers, using octyl spacers creates a meshlike water network, yielding ion conductivity equal to 30.6 mS/cm at room temperature. For SEBS-based polymers, the nonmodified form is sufficient to produce ion-conducting pathways. Adding hydrophobic spacers further enhances the nanosegregation, and the membranes provide similar conductivity at a lower ion exchange capacity and water content. Adding hydrophilic spacers, however, has negative impacts on the ion transport. The side chains are in the stretched configurations, which sterically hinder the mobility of water and hydroxide ions. Such a resistance can be overcome by adapting multication side-chain designs, where large water channels are formed, yielding ion conductivity as high as 32.8 mS/cm.Commonly, thermally activated delayed fluorescence (TADF) emitters present a twisted donor-acceptor structure. Here, electronic communication is mediated through-bond via π-conjugation between donor and acceptor groups. A second class of TADF emitters are those where electronic communication between donor and acceptor moieties is mediated through-space. In these through-space charge-transfer (TSCT) architectures, the donor and acceptor groups are disposed in a pseudocofacial orientation and linked via a bridging group that is typically an arene (or heteroarene). In most of these systems, there is no direct evidence that the TSCT is the dominant contributor to the communication between the donor and acceptor. Herein we investigate the interplay between through-bond localized excited (LE) and charge-transfer (CT) states and the TSCT in a rationally designed emitter, TPA-ace-TRZ, and a family of model compounds. From our photophysical studies, TSCT TADF in TPA-ace-TRZ is unambiguously confirmed and supported by theoretical modeling.The synthesis and thermoresponsive properties of surface-attached poly(N-isopropylacrylamide)-co-N,N'-methylene bisacrylamide (PNIPAM-co-MBAM) networks are investigated. The networks are formed via SI-ARGET-ATRP ("grafting-from") on thiol-based initiator-functionalized gold films. This method is reliable, well controlled, fast, and applicable to patterned surfaces (e.g., nanopores) for networks with dry thicknesses >20 nm. Surface-attached PNIPAM-co-MBAM gels are swollen below their volume phase transition temperature but above collapse without complete expulsion of water (retain ∼50 vol %). The swelling/collapse transition is studied using complementary SPR and QCMD techniques. The ratio between swollen and collapsed heights characterizes the thermoresponsive behavior and is shown to not depend on network height but to vary with MBAM content. The higher the proportion of the crosslinker, the lower the magnitude of the phase transition, until all responsiveness is lost at 5 mol % MBAM. The temperature range of the transition is broadened for more crosslinked PNIPAM-co-MBAM gels but remains centered around 32 °C. Upon reswelling, less crosslinked networks display sharp transitions, while for those containing ≥3 mol % MBAM, transitions remain broad. This tunable behavior persists for gels on nanostructured gold surfaces. Investigating PNIPAM-co-MBAM networks on gold plasmonic nanowell arrays is a starting point for expanding their scope as thermo-controlled nanoactuators.The size effect on the activity of a catalyst has been a focal issue since ideal catalysts were pursued, whereas that on the degradation of a catalyst, by reaction intermediates such as CO, is little discussed. We demonstrate that the dehydrogenation of methanol-d4 on supported Rh nanoclusters precovered with CO (Rh-CO clusters) was obstructed, indicated by a decreased production of CO and D2; the obstructive effect exhibits a remarkable dependence on the cluster size, with a minimum at a cluster diameter near 1.4 nm. The decreased production arose from a decreased reaction probability controlled by the increased activation energy for each dehydrogenation step (including formation of methoxy-d3), adsorption energies of CO, and repulsion from the CO array on the Rh-CO surface. The effects of these factors in deactivating the clusters varied separately with the cluster size. Consequently, the size effect on the CO poisoning should be taken into account in engineering the cluster size to optimize the catalytic performance.In this study, 2,3-dicyanopyrazino phenanthrene (DCPP), a commodity chemical that can be prepared at an industrial scale, was used as a photocatalyst in lieu of Ru or Ir complexes in C-X (X = C, N, and O) bond-forming reactions under visible-light irradiation. In these reactions, [DCPP]n aggregates were formed in situ through physical π-π stacking of DCPP monomers in organic solvents. These aggregates exhibited excellent photo- and electrochemical properties, including a visible light response (430 nm), long excited-state lifetime (19.3 μs), high excited-state reduction potential (Ered([DCPP]n*/[DCPP]n·-) = +2.10 V vs SCE), and good reduction stability. The applications of [DCPP]n aggregates as a versatile visible-light photocatalyst were demonstrated in decarboxylative C-C cross-coupling, amidation, and esterification reactions.Maintaining fast charging capability at low temperatures represents a significant challenge for supercapacitors. The performance of conventional porous carbon electrodes often deteriorates quickly with the decrease of temperature due to sluggish ion and charge transport. Here we fabricate a 3D-printed multiscale porous carbon aerogel (3D-MCA) via a unique combination of chemical methods and the direct ink writing technique. 3D-MCA has an open porous structure with a large surface area of ∼1750 m2 g-1. At -70 °C, the symmetric device achieves outstanding capacitance of 148.6 F g-1 at 5 mV s-1. Significantly, it retains a capacitance of 71.4 F g-1 at a high scan rate of 200 mV s-1, which is 6.5 times higher than the non-3D printed MCA. These values rank among the best results reported for low temperature supercapacitors. These impressive results highlight the essential role of open porous structures for preserving capacitive performance at ultralow temperatures.Much of our understanding of proteins and proteomes comes from the traditional protein structure-function paradigm. However, in the last 2 decades, both computational and experimental studies have provided evidence that a large fraction of functional proteomes across different domains of life consists of intrinsically disordered proteins, thus triggering a quest to unravel and decipher protein intrinsic disorder. Unlike structured/ordered proteins, intrinsically disordered proteins/regions (IDPs/IDRs) do not possess a well-defined structure under physiological conditions and exist as highly dynamic conformational ensembles. In spite of this peculiarity, these proteins have crucial roles in cell signaling and regulation. To date, studies on the abundance and function of IDPs/IDRs in viruses are rather limited. To fill this gap, we carried out an extensive and thorough bioinformatics analysis of 283 000 proteins from 6108 reference viral proteomes. We analyzed protein intrinsic disorder from multiple perspectives, such as abundance of IDPs/IDRs across diverse virus types, their functional annotations, and subcellular localization in taxonomically divergent hosts.
Homepage: https://www.selleckchem.com/products/U0126.html